改性羟基磷灰石/聚乳酸(PLLA)复合材料的制备及细胞毒性
戴延凤；张好宾；魏俊超；吴婷珍
南昌大学化学系
Preparation and cytotoxicity of modified hydroxyapatite/Poly(L-lactide) composites
DAI Yan-feng,ZHANG Hao-bin,WEI Jun-chao,WU Ting-zhen
摘要 制备了一种表面接枝聚(γ-苄基-L-谷氨酸)的改性纳米羟基磷灰石(PBLG-g-HA),利用红外光谱(FT-IR)、X射线光电子能谱(XPS)证明了聚(γ-苄基-L-谷氨酸)(PBLG)成功的接枝在羟基磷灰石表面,TGA结果显示PBLG的接枝量为33.6%。通过溶剂复合法制得了PBLG-g-HA/PLLA复合材料,并通过MTT法对所制备的复合材料的细胞毒性进行了研究。结果表明,PBLG-g-HA/PLLA复合材料具有良好的生物相容性、能够促进成骨细胞增殖。 更多 还原
关键词 ：
羟基磷灰石 ,
表面改性 ,
聚乳酸 ,
复合材料 ,
细胞毒性
Abstract ：A kind of poly(γ-benzyl-L-glutamate) modified hydroxyapatite was prepared.Fourier transform infrared(FT-IR) spectroscopy,X-ray photoelectron spectroscopy(XPS) showed that PBLG was successfully grafted.The thermal gravimetric analysis(TGA) results indicated that the surface grafting amount of PBLG-g-HA was about 33.6%.PBLG-g-HA/poly(L-lactide)(PLLA) nanocomosites were prepared via solvent-mixing method.Cell culture tests and MTT assessments showed that PBLG-g-HA/PLA composites possessed excellent biocompatibility and promote the adhesion and proliferation of osteoblast.
Key words ：
hydroxyapatite
surface modification
poly(L-lactide)
composites
cytotoxicity
基金资助: 江西省自然科学基金资助项目(20114BAB213009)
[1]
管国阳； 孙滔； 陈涛. 切割深度对复合材料胶接试验强度的影响
[2]
王伟； 李洪忠； 王慧； 武斌. 不同牙本质脱敏药物临床远期疗效的对照研究
[3]
刘晓红； 毛艳红； 潘逸凡. 谷氨酸接枝纳米碳酸钙的合成
[4]
刘晓红； 毛艳红； 潘逸凡. 二氧化硅包覆纳米碳酸钙的合成
[5]
鲍垚； 王肖庆； 陈玉凤. CdS纳米粒子/层状硅酸盐复合物的合成及光学性质的研究
[6]
周泽华； 辛勇； 曾效舒. 铸钢碳纳米管复合材料的机械性能
[7]
章丹亭； 刘莹； 殷艳飞； 刘小龙. C/C复合材料的摩擦磨损行为研究
[8]
曾建华；熊龙；李经堂；严亮；凌蒙； . 纳米羟基磷灰石复合重组人骨形态发生蛋白-2人工骨治疗骨缺损的研究
[9]
边风根； 曾莉； 严兆华. 聚二甲基硅氧烷弹性体的表面改性及生物相容性
[10]
郑夏莲；朱正吼；宋晖； . 铁基非晶粉体/S-玻璃纤维/环氧树脂复合材料板制备及其吸波性能
[11]
邓文君； 高立军. 二氧化钌/石墨烯纳米复合材料的制备及其电化学性能
[12]
余桂英； 李小兵； 罗超. 溶液共混法制备聚氨酯/碳纳米管复合材料的工艺研究
[13]
龚良贵; 侯瑾; 李情. 面内载荷作用下复合材料层合板非线性屈曲
[14]
刘晓红; 邹美捷; 许春晓; 柯春兰. 溶胶-凝胶法所制LiCoPO_4及其掺碳材料的电化学性能
[15]
刘东京; 邱俊明; 邱祖民. 阻燃硅橡胶材料的制备与性能初探
2012, Vol. 36 