王晓俊; 吴光辉; 邹建平; 欧阳文
江西科技师范学院理工学院； 南昌航空大学环境与化学工程学院； 南昌大学后勤集团；
WANG Xiao-jun1,WU Guang-hui2,ZOU Jian-ping2,OU Yang-wen3(1.Institute of Technology,Jiangxi Science & Technology Normal University,Nanchang 330013,China; 2.School of Environment and Chemical Engineering,Nanchang Hangkong Uiniversity,Nanchang 330063,China;
摘要 以普通钠钙载玻片为基片,采用溶胶一凝胶法制备了ZnO薄膜。XRD结果表明薄膜C轴取向明显,SEM显示颗粒大小为20nm左右,紫外可见光测定说明薄膜在可见光区域透光率基本为86%左右,透光率好,而接触角实验结果表明紫外照射ZnO薄膜30min,水滴能完全在薄膜上铺展,接触角为0°,具有很好
关键词 ：
亲水防雾 ,
光催化 ,
ZnO薄膜
Abstract ：ZnO thin films coated on soda-lime glass slide were prepared by sol-gel process.The XRD results revealed that the ZnO thin films was of obvious c-axis orientation.The grain sizes were about 20 nm as abserved by SEM.The transmission values were observed up
Key words ：
ZnO thin film
photoinduce
hydrophilicity and antifogging ability；
出版日期: 2011-10-28
引用本文:
王晓俊; 吴光辉; 邹建平; 欧阳文. ZnO薄膜光催化亲水防雾[J]. 南昌大学学报（理科版）, 2011, 35(05): 1-.
链接本文:
http://qks.ncu.edu.cn/Jwk_xblxb/CN/ 或 http://qks.ncu.edu.cn/Jwk_xblxb/CN/Y2011/V35/I05/1
[1]
彭惠琛； 彭绍琴； 李越湘. 污染物为电子给体Cd0.5Zn0.5S固溶体光催化分解水制氢
[2]
涂盛辉； 戴策； 胡亚平； 王犇； 杜军. Pt-RGO-Cu2 O/TiO2 催化剂的制备及光催化制氢活性
[3]
涂盛辉； 骆中璨； 林立； 刘婷； 王犇； 杜军； 邱俊明. CuO-CeO2 /ZSM-5催化剂的制备及其降解酸性大红GR的研究
[4]
冯斐； 胡兆吉； 赖劲虎； 吴婷. 光催化内循环耦合MBR处理垃圾渗滤液
[5]
彭绍琴；高丹；詹志康；易婷；李越湘； . 葡萄糖为电子给体NaCl盐水体系Cdx Zn1-x S固溶体光催化制氢简
[6]
赵勇; 俞进; 于鹏; 侯硕; 梁晓军; 方利广; 盛广沪. 退火温度对ZnO薄膜结构和内应变的影响
[7]
吕亚洲; 邱祖民. Pb2+-SiO_2-TiO_2复合催化剂的制备及光催化性能
[8]
高丹; 李志龙; 彭绍琴; 李越湘. 乙二醇作电子给体的Pt/TiO_2光催化海水制氢反应
[9]
彭绍琴; 刘雄鹰; 李越湘. 伊红-Y敏化硫掺杂TiO_2的制备及可见光光解水制氢性能
[10]
俞慧芳; 方先平; 俞美芳; 杨珊琳; 陈文有; 邱祖民. TiO_2光催化氧化含酚废水的工艺研究
[11]
谢艳招; 李越湘; 彭绍琴. 利用含葡萄糖废水光催化制氢
[12]
雷雪飞; 刘文占; 张洪林; 蒋林时. 纳米二氧化钛粉体光催化染料脱色的研究
[13]
弓晓峰; 简敏菲; 刘春英. TiO_2光催化氧化固定化技术在水处理中的应用
[14]
彭绍琴; 李越湘. 二氧化钛光催化回收金属银离子
[15]
弓晓峰; 刘春英; 樊华; 祝林慧. 甲基橙溶液的光催化氧化研究
2011, Vol. 35 