改进光纤布拉格光栅传感性能的方法
南昌大学机电工程学院江西省机器人及焊接自动化重点实验室
Improvement Method of FBG Sensor Performance
ZHANG Hua,XIAO Li-li,FENG Yang,RAO Chun-fang,PENG Xing-ling
摘要 为了改善金属化保护后光纤Bragg光栅(FBG)的传感性能,采用化学镀后随恒温水浴箱自然冷却的方法减小温度突变。实验表明:改进后化学镀前后其透射谱3 dB带宽为0.129 nm,没有改变,峰值损耗只降低了3.42%,同时其温度传感迟滞误差为1.85%,测量值中最大正反行程差值折算成温度约为1.48℃。
关键词 ：
光纤Bragg光栅 ,
带宽 ,
损耗 ,
迟滞误差 ,
温度传感
Abstract ： In order to improve the performance of metal coated Fiber Bragg Grating(FBG) sensor,the electroless plating FBG was cooled slowly to room temperature with the water in thermostatic bath.It showed that 3 dB bandwidth was 0.129 nm without any change,the peak loss was only reduced by 3.42%,at the same time the hysteresis error was 1.85%,the biggest difference value between positive and negative trip was approximately 1.48 ℃ when it was converted into temperature.
Key words ：
fiber Bragg grating(FBG)
bandwidth
loss
hysteresis error
temperature sensing
出版日期: 2012-03-28
[1]
黄志红. 对称金属包覆波导吸收传感理论分析
[2]
袁义生； 李怀谷； 朱本玉； 张育源. 一种新型恒流源驱动电路及参数设计
[3]
胡从立；陈金平；徐敏； . 基于改进蚁群算法的含分布式电源的配电网重构
[4]
汪晶慧； 陈为. 矩形波激励下磁芯损耗测量中绕组损耗的测量
[5]
罗广圣; 姜贵文; 李建德; 周正有. Cu离子掺杂Ni-Zn铁氧体的结构和介电性能
[6]
罗广圣; 李建德; 姜贵文; 周正有. Ni-Zn铁氧体的制备及其电磁性能
[7]
徐玉华; 杨维汉. 全空间弹性介质系统的非因果扰动
[8]
殷平; 李曼丽. 基于禁忌搜索的同步开关法在配电网重构中的应用
[9]
罗晓梅; 万国金. 对数距离路径损耗下的协作分集
[10]
徐申翔; 刘南生; 张华. 光纤温度传感器原理及应用
[11]
黄志超; 包忠诩; 周天瑞. 有限元节点编号优化
[12]
谢本亮. Hg_2Br_2声光器件的换能器带宽和镀层厚度的确定
[13]
曾勍炜. 一种传输实时证券行情的技术
[14]
费跃农; 吴志强. 逆变电源开关损耗的分析与对策
[15]
何明春; 由敬舜; 杨德品. 有限元加密中的带宽极小化
2012, Vol. 34 